Synthesis and Characterization of Polyethylene Terephthalate–Derived Graphene Reinforced Hydroxyapatite–Kaolin Composites for Bone Tissue Engineering | ||
| Innovations in Materials: Current & Future | ||
| دوره 1، شماره 1، فروردین 2026، صفحه 12-23 اصل مقاله (1.4 M) | ||
| نوع مقاله: Original Paper | ||
| شناسه دیجیتال (DOI): 10.22075/imcf.2025.39269.1048 | ||
| نویسندگان | ||
| Daniel Arinze Ozieme* 1؛ Emmanuel Anegbe2 | ||
| 1Department of Industrial Chemistry, College of Science and Technology, Covenant University Ota Ogun State, Nigeria | ||
| 2FunGlass – Centre for Functional and Surface Functionalized Glass, Študentská 2, 911 50 Trenčín, Slovakia | ||
| تاریخ دریافت: 12 مهر 1404، تاریخ بازنگری: 05 آبان 1404، تاریخ پذیرش: 05 آذر 1404 | ||
| چکیده | ||
| This study presents the synthesis and physicochemical characterization of a graphene–hydroxyapatite–kaolin (GHK) composite designed for potential artificial bone applications. Graphene was derived from recycled polyethylene terephthalate (PET) waste through pyrolysis at 600 °C, while hydroxyapatite (HAp) was synthesized from calcined eggshells and combined with kaolin clay. The powders were compacted and sintered at 1100 °C to produce three formulations. Porosity and density values were 22.5% and 2.75 g/cm³ for GHK-A, 19.8% and 2.85 g/cm³ for GHK-B, and 26.3% and 2.62 g/cm³ for GHK-C within the ASTM C373 standard range (porosity: 0–30%, density: 2.4–3.0 g/cm³). GHK-B exhibited the lowest porosity and highest density, indicating compactness and mechanical strength suitable for load-bearing bone applications. Fourier-transform infrared spectroscopy (FTIR) confirmed bands of PO₄³⁻ at 1030–960 cm⁻¹, OH⁻ stretching at 3570 cm⁻¹, and Si–O vibrations near 1100 cm⁻¹, validating the successful integration of HAp, kaolin, and graphene phases. X-ray diffraction (XRD) patterns showed distinct crystalline peaks corresponding to HAp planes at 2θ = 25.9°, 31.8°, and 39.9°, with GHK-B exhibiting sharper peaks than GHK-A and GHK-C, indicating improved crystallinity and phase purity. Scanning electron microscopy (SEM) revealed an interconnected porous network with flake-like graphene layers reinforcing the HAp-kaolin matrix suitable for osteoblast infiltration and nutrient transport. The synergy between graphene’s conductivity, HAp’s bioactivity, and kaolin reinforcement produced a composite with balanced structural properties. GHK-B demonstrated the most promising material combining cortical bone-like density (2.85 g/cm³), controlled porosity (19.8%), and superior crystalline structure suggesting its potential as a mechanically bioactive scaffold for bone tissue regeneration. | ||
| کلیدواژهها | ||
| Graphene؛ Hydroxyapatite؛ Kaolin؛ Waste Recycling؛ Artificial Bone؛ Bone Tissue Engineering؛ Composites | ||
|