Fallah Samakosh, Saleh, Bahari, Ali, Fallah Hamidabadi, Vaheed, Milani Moghaddam, Hossain. (1402). Synthesis of coated iron oxide nanoparticles and feasibility study of their use in magnetic hyperthermia. هنرهای کاربردی, 3(1), 67-72. doi: 10.22075/ppam.2023.31537.1061
Saleh Fallah Samakosh; Ali Bahari; Vaheed Fallah Hamidabadi; Hossain Milani Moghaddam. "Synthesis of coated iron oxide nanoparticles and feasibility study of their use in magnetic hyperthermia". هنرهای کاربردی, 3, 1, 1402, 67-72. doi: 10.22075/ppam.2023.31537.1061
Fallah Samakosh, Saleh, Bahari, Ali, Fallah Hamidabadi, Vaheed, Milani Moghaddam, Hossain. (1402). 'Synthesis of coated iron oxide nanoparticles and feasibility study of their use in magnetic hyperthermia', هنرهای کاربردی, 3(1), pp. 67-72. doi: 10.22075/ppam.2023.31537.1061
Fallah Samakosh, Saleh, Bahari, Ali, Fallah Hamidabadi, Vaheed, Milani Moghaddam, Hossain. Synthesis of coated iron oxide nanoparticles and feasibility study of their use in magnetic hyperthermia. هنرهای کاربردی, 1402; 3(1): 67-72. doi: 10.22075/ppam.2023.31537.1061

Synthesis of coated iron oxide nanoparticles and feasibility study of their use in magnetic hyperthermia

Progress in Physics of Applied Materials
دوره 3، شماره 1 - شماره پیاپی 4، بهمن 2023، صفحه 67-72    اصل مقاله (614.78 K)
نوع مقاله: Original Article
شناسه دیجیتال (DOI): 10.22075/ppam.2023.31537.1061
نویسندگان
Saleh Fallah Samakosh1، 2؛ Ali Bahari* 3، 2؛ Vaheed Fallah Hamidabadi3، 2؛ Hossain Milani Moghaddam3، 4
1Department of Solid State Physics, University of Mazandaran, Babolsar, Iran.
2Nanoelectronic Research Laboratory, Faculty of Sciences, Department of Physics, University of Mazandaran, Babolsar, Iran.
3Department of Solid State Physics, University of Mazandaran, Babolsar, Iran.
4Molecular Electronic Laboratory, University of Mazandaran, Babolsar, Iran.
چکیده
The unique properties of magnetic nanoparticles have made them useful and important particles for use in various fields, especially in heat-based applications. This research presents a hopeful facet of magnetic hyperthermia by superparamagnetic Fe3O4/Alumina nanoparticles. We synthesized Fe3O4/Alumina nanoparticles of different sizes by sonochemical method and evaluated their ability to generate heat. We found by characterizations with Field emission scanning electron microscopy (FE-SEM), X-ray diffraction technique (XRD), and Transmission electron microscopy (TEM) the samples to be of spherical shapes and spinel structure whose diameter could be controlled in the range from 15 to 25 nm. The magnetic behavior of the samples determined using a vibration sample magnetometer (VSM) showed hysteresis loops with a coercivity (HC) close to zero, suggesting superparamagnetic behavior at room temperature. The saturation magnetization (MS) for sample 3 after synthesis is 23 emu/g. We also investigated the potential of the samples for magnetic hyperthermia using alternating magnetic fields at various frequencies. Samples 1, 2, and 3 achieved heat production rates of 0.22 °C/min, 0.41 °C/min, and 0.62 °C/min respectively under an alternating magnetic field with an amplitude of 120 Oe and a frequency of 250 kHz. 
کلیدواژه‌ها
Magnetic hyperthermia؛ Fe3O4؛ Alumina؛ Core@shell structure؛ Superparamagnetic
مراجع
آمار
تعداد مشاهده مقاله: 471
تعداد دریافت فایل اصل مقاله: 562
دانشگاه سمنان
پیوندهای مفید
آمار
تعداد نشریات22
تعداد شماره‌ها722
تعداد مقالات10,383
تعداد مشاهده مقاله72,838,795
تعداد دریافت فایل اصل مقاله64,535,415